OHMEGA-PLY RCM PROPERTIES AND SPECIFICATIONS
|
|
|
|
|
|
REMARKS & CONDITIONS
|
Sheet Resistivity
|
25
(Standard)
|
50
(Standard) |
100
(Standard) |
250
(Pre-Production) |
1000
(R&D) |
|
Material Tolerance
|
+/-5
|
+/-5
|
+/-5
|
+/-10
|
+/- 10
|
|
Load Life Cycling Test (R%)
|
5
|
5
|
5
|
0.5
(for 1000 hrs)
|
0.75
(for 1000 hrs)
|
MIL-STD-202-108I
Ambient Temp: 70C
On Cycle: 1.5 hrs
Off Cycle: 0.5 hrs
Length Of Test: 10000 hrs
|
Current Noise Index in db
|
<40
|
<40
|
<40
|
<40
|
<40
|
MIL-STD-202-308
Voltage Applied
25 ohm/sq: 5.6 V
100 ohm/sq: 7.9 V
|
Short Time Overload
|
0
|
0
|
0
|
n/a
|
n/a
|
MIL-R-10509 Method 4.6.6
Power: 2.5 X Rated
Time: 5 Sec
|
Resistance Temperature characteristic(RTC)
|
50
|
75
|
100
|
100
|
100
|
MIL-STD-202-304
Hot Cycle: 25 , 50, 75 & 125
Cold Cycle: 25, 0, -25 & -55
|
Humidity Test
|
0.5
|
0.75
|
1.0
|
2.0
|
2.0
|
MIL-STD-202-103
Temp: 40 deg C
RH: 95 %
Time: 240 hrs
|
Thermal Shock
|
-0.5
|
-0.1
|
1.0
|
n/a
|
n/a
|
MIL-STD-202-107
No Cycles: 25
Hot Cycle Temp: 125 deg C
Cold Cycle Temp: -65 deg C
|
Hot Oil
|
0.1
|
0.25
|
0.5
|
n/a
|
n/a
|
IPC-TM-650 Method 2.4.6
Temp: 260 deg C
Immersion: 20 Sec
|
Solder Float
|
0.5
|
0.75
|
1.0
|
0.5
|
1.0
|
MIL-STD-202-210
Temp: 260 deg C
Immersion: 20 Sec
|
Resistance To Solvent
Toluence 1-1-1:
Trichloroethan:
Acetone:
Freon:
|
0.2
0.0
0.2
0.0
|
n/a
|
n/a
|
n/a
|
n/a
|
MIL-STD-202-215A
Immersion: 15 Min
|
Tape Pull Test
|
Good
|
Good
|
Good
|
Good
|
Good
|
Classifications:
Good--- No Voids
Fair--- Some Voids
Bad--- Many Voids
|
Peel Strength (lbs/in)
|
Spec
|
Spec
|
Spec
|
Spec
|
Spec
|
Spec > 5 lbs/in
|
Capacitance(pF)
(at 5 Ghz)
|
~1
|
~1
|
~1
|
~1
|
n/a
|
|
Inductance(nH)
(at 5 Ghz)
|
~0.6
|
~0.6
|
~0.6
|
~0.6
|
n/a
|
|